ABSTRACT Water pollution from synthetic dyes and oil spills has a significant impact on the environment and living species. Here, we developed a low-cost, environmentally friendly and easily

biodegradable magnetic hybrid bio-sponge nanocomposite from renewable resources such as collagen and cellulose (Kenaf fibre cellulose–collagen, KFCC). We loaded it with magnetic bimetallic

Fe3O4@TiO2 (BFT) NPs to produce a photocatalyst material (KFCC-BFT) for the treatment of colored wastewater as well as a sorbent for oil–water separation. The characterization of the

bimetallic BFT NPs by XRD, HRTEM and VSM showed the deposition of TiO2 particles onto the surface of Fe3O4 with lattice interlayers spacing of 0.24 and 0.33 nm for Fe3O4 and TiO2,

respectively with ferromagnetic property. The UV–vis diffuse reflectance spectra result indicated that the band gap energy of bio-sponges decreases with the increase of the bimetallic

moiety. The photocatalytic efficiency of the as-prepared magnetic hybrid bio-sponge in the degradation of crystal violet dye was up to 91.2% under visible light conditions and 86.6% under

direct sunlight exposure. Furthermore, the magnetic hybrid bio-sponge was used to separate motor oil from water (> 99%) and had a high oil sorption capacity of 46.1 g/g. Investigation of

the recyclability and reusability performance for 9 cycles revealed that the bio-sponge had a high sorption capacity for up to 5 cycles. Our results suggest that the bio-polymer-supported

BFT hybrid nanocomposite is a cost-effective and easily biodegradable photocatalyst and has great potential for real-field environmental remediation applications. SIMILAR CONTENT BEING

VIEWED BY OTHERS DEVELOPMENT OF AN ANTIMICROBIAL INORGANIC POLYMER BASED ON FLY ASH AND METAKAOLIN INCORPORATED BY NANO-TIO2 FOR REACTIVE DYE REMOVAL Article Open access 14 November 2023 A

SMART AND SUSTAINABLE PATHWAY FOR ABATEMENT OF SINGLE AND BINARY MIXTURES OF DYES THROUGH MAGNETICALLY RETRIEVABLE CA4FE9O17 ANCHORED ON BIOCHAR MATRIX Article Open access 09 August 2023

ENHANCED METHYLENE BLUE ADSORPTION USING SINGLE-WALLED CARBON NANOTUBES/CHITOSAN-GRAFT-GELATIN NANOCOMPOSITE HYDROGELS Article Open access 19 August 2024 INTRODUCTION Environmental

pollution, predominantly water pollution, is currently a major global threat imposing severe hazards to both human and ecosystem health. Water pollution is a severe concern for all

stakeholders including society, public authorities, and industries1. The rapid development of industries such as textile, leather, paint, paper, printing, and plastic as well as offshore oil

and gas leads to the increase in the discharge of various pollutants into water2. One of the most common pollutants are organic pollutants such as organic dyes, agrochemicals, phenols,

cosmetics, pharmaceutical and petrochemical wastes, which are very hazardous to aquatic organisms and damaging whole ecosystems due to the reduction of the amount of dissolved oxygen in the

water in their oxidative decomposition process3,4. Amongst various organic pollutants, soluble dyes and insoluble oils are causing severe damage to the ecosystem. Synthetic dyes are the most

used in industries and are composed of polyaromatic molecules containing one or more azo bonds N=N–) that give permanent color to materials. The application of synthetic dyes is diverse

ranging from textile and paint to leather industries5,6,7. The unused synthetic dyes present in water are toxic, carcinogenic, and mutagenic and may affect the aquatic environment and human

beings, even at a low-level concentration5,6. It is challenging to completely remove colour pollutants from water using traditional wastewater treatment techniques such as absorption and

oxidation8,9. In general, effluents containing soluble contaminants, solids, colloids, organic matter and minerals are removed through various physical, chemical and/or biological

techniques10. For the removal of organic contaminants from contaminated effluents, conventional water treatment techniques such as air flotation, precipitation, coagulation, oxidation,

adsorption, ion exchange, membrane filtration, etc., are popular11,12. Each treatment method has its own advantages and limitations such as operational costs, efficiency, functionality,

dependability, eco impression, post-treatment requirements, and also the creation of sludge and toxic by-products. For intense, photocatalytic degradation has been considered an effective

and advanced approach to removing the dyes from the wastewater owing to its advantages such as low cost, non-selective degradation and operating with conventional separation technology

without further secondary pollution13. Among different semiconductor photocatalysts developed for the removal of organic contaminants in wastewater, TiO2 nanoparticles (NPs) have been

extensively used owing to non-toxicity, low cost and availability, excellent chemical and thermal stability, high catalytic activity, and excellent carrier properties14,15,16. However, the

TiO2 NPs have some drawbacks that restrict their real field uses as photocatalysts for wastewater treatment, including agglomeration, the high recombination rate of photo-generated

electron–hole pairs and tough recovering due to smaller particle sizes17,18,19. Moreover, the intrinsic large bandgap energy (3.23 eV) limits the use of TiO2 NPs for solar irradiation

applications20. Bimetallic Fe3O4@TiO2 (BFT) NPs have been extensively investigated to overcome the separation or recovery problem of TiO221. Magnetic Fe3O4 NPs based photocatalysts provide a

real field practicable method to recover magnetic particles from the reaction media as well as possible reuse of the catalyst. Additionally, magnetic Fe3O4 NPs have superior magnetism,

excellent compatibility, low cytotoxicity despite high loading and can speed up the transfer of photo-induced electrons between (Fe3+, Fe2+) to increase the photocatalytic activity of

TiO222,23. Water pollution by oil spills can happen during the process of offshore activity by accidents involving tankers, barges, pipelines, refineries, drilling operations, and storage

facilities. Oil spills in water bodies not only destroyed aquatic organisms such as sea birds, mammals, algae, etc. but the sand on the coastline was also severely polluted. Following a

large oil spill, the effects on ecosystems and economies can last for decades, making the problem of oil/water separation a global challenge24,25,26,27. Several methods can be used to

control and eradicate oil leaks from water such as oil bloom or containment bloom, which is a temporary floating barrier method used to contain oil, a skimmer using skimming agents to skim

oil from the surface of the water, in situ burning to fire away oil slicks at the surface of the water, chemical dispersants to break the emulsion oil/water and physical sorbents to absorb

oil. Among the aforementioned methods for oil/water separation, physical sorbents have gained special attention amongst researchers and industry communities owing to their low density, high

3D porous material (sponges or aerogels), large surface area, surface roughness, tortuosity, recyclability, complete removal and absence of secondary pollution28,29,30,31. Hence, an

effective photocatalytic method for the removal of both dyes and oils from wastewater is ideally required. In recent years, native cellulose and naturally derived nano cellulose have been

extremely used in research as renewable and sustainable materials for the preparation of sorbent sponges suitable for the photodegradation of organic pollutants and oil/water emulsion

separation. Due to its numerous beneficial features such as renewability, biodegradability, lightweight, large surface area, good mechanical strength, thermal stability and non-toxicity,

extracted cellulose from the lignocellulosic fiber is frequently used as filler or reinforcing material for the preparation of composites, paper and textile industries, automobiles and 3D

scaffold biomaterials. Super-hydrophobic and super-hydrophilic/super-oleophobic cellulose sponges have been fabricated for oil/water separation26,28,29. In the same trend of preparing

bio-based advanced materials, collagen which is a by-product waste from the leather industry has been recently used for the preparation of sorbent sponges for wastewater treatment.

Collagen-based biomaterials have been prepared for various applications including scaffolds for tissue engineering32,33,34 bioengineered scaffolds for scarless healing of deep burns35,

conducting hybrid aerogels36, and water remediation6 due to its wide availability, high biocompatibility and biodegradability. Each year, a huge amount of collagen-containing waste is

disposed into the environment from leather industries, therefore, preparing environmentally free and cost-effective bio-based materials from leather waste is highly feasible and viable.

Herein, a hybrid nanocomposite comprising cellulose and collagen biopolymeric matrices embedded with bimetallic Fe3O4@TiO2 NPs was prepared with multifunctional properties for environmental

remediation applications. Magnetic bimetallic Fe3O4@TiO2 NPs were synthesized by mixing the pre-synthesized Fe3O4 NPs with titanium precursor followed by chemical reduction. Cellulose was

extracted from Kenaf fibers (Kenaf fiber cellulose, KFC) whereas collagen was extracted from cowhide trimming wastes and combined to form a Kenaf fiber cellulose–collagen (KFCC) matrix.

Combining BFT with KFCC yielded bio-based Kenaf fiber cellulose–collagen nanocomposite sponge incorporated with BFT NPs (KFCC-BFT) was characterized for their structural and functional

properties and further studied for wastewater remediation applications. MATERIALS AND METHODS MATERIALS Kenaf fiber was extracted from the kenaf tree (cultivated traditionally by farmers for

making ropes to tie piles of rice after harvest for storage) collected in Issakaha village, from the Korhogo region, Côte d’Ivoire (Ivory Coast). All the plant experiments were in

compliance with relevant institutional, national and international guidelines and legislation. Freshly flayed hides was purchased from the local slaughterhouse, Chennai, India. Raw cowhide

trimming wastes were collected from the leather processing unit at CSIR-Central Leather Research Institute, Chennai, India. Hide powder was prepared from raw cowhide trimming wastes and were

treated using the conventional process to remove the unwanted hair and flesh based on our previous report37. All chemicals were of analytical grade and were used without any further

purification. Chemicals used were sodium hydroxide (SD Fine Chem Limited, 98%), sodium chlorite (LOBA Chemie, 80%), sodium sulfite anhydrous (EMPARTA, 98%), acetic acid (SRL, 99.9%), acetone

(SD Fine Chem Limited), citric acid, titanium (IV) isopropoxide (Sigma Aldrich, 97%), iron (II) sulphate (SD Fine Chem Limited, 99%), iron (III) sulphate (SD Fine Chem Limited, 75%),

ammonia (Rankem), isopropanol (Qaligens, 70%), ethanol (Hayman, 100%) and nitric acid (SD Fine Chem Limited, 69–72%). EXTRACTION OF CELLULOSE FROM KENAF FIBERS Kenaf fibers were dried and

cut into small pieces. 20 g of dried fibers were boiled with 300 mL of 6% NaOH (w/v) for 1 h. The pre-treated fibers were washed and ground in a laboratory mixer for 3 min to produce

pulp-like fibers. Then, the delignification process was carried out by bleaching the pulp-like fibers with 300 mL 0.7% (w/v) sodium chlorite at pH 4, adjusted with 5% acetic acid and boiled

for 3 h. The partially lignin-free fiber residue was washed with distilled water to neutral pH. The neutralized fiber residue was boiled with 300 mL 5% (w/v) sodium sulfite for 5 h to remove

the lignin completely as well as hemicellulose partially. The obtained holocellulose was boiled with 300 mL 17.5% (w/v) sodium hydroxide solution for 5 h to remove the hemicelluloses. The

isolated cellulose was washed with distilled water until neutral pH and air-dried38. SYNTHESIS OF MAGNETIC BFT NANOPARTICLES SYNTHESIS OF FE3O4 NANOPARTICLES The Fe3O4 NPs were synthesized

by the co-precipitation method. Briefly, 250 mL of the Erlenmeyer flask containing 100 mL of 0.1 M FeCl3 and 100 mL of 0.05 M FeSO4.7H2O were stirred for 30 min at 60 °C. Then, 25% of

ammonia solution was added drop by drop until the pH reaches 10, leading to dark yellow precipitate. The obtained Fe3O4 NPs were washed thoroughly with distilled water to neutral pH and

separated using centrifugation for 20 min at 10,000 rpm. The purified NPs were dried in a hot air oven at 100 °C for 8 h and calcinated at 500 °C for 2 h under a nitrogen environment.

SYNTHESIS OF TIO2 NANOPARTICLES For the synthesis of TiO2 NPs using the sol − gel method, 5 mL of titanium (IV) isopropoxide was added to 20 mL of ethanol and the mixture was stirred at 500 

rpm at 60 °C for 30 min. Then, a mixture of 20 mL of ethanol/water (1:1) and 2 mL of HNO3 (72%) was added dropwise. The resulting mixture was stirred at 1000 rpm for another 3 h at 100 °C to

form a gel. The obtained product was centrifuged at 10,000 rpm for 20 min. The collected pellet was washed with distilled water and then with ethanol and kept at 100 °C in a hot air oven

for 8 h and calcinated at 500 °C for 2 h under a nitrogen environment. SYNTHESIS OF MAGNETIC BFT NANOPARTICLES Magnetic bimetallic Fe3O4@TiO2 NPs were synthesized through the chemical

reduction method. In this procedure, 5 mL of titanium (IV) isopropoxide was dissolved in 25 mL isopropanol. Subsequently, 0.2 g of the pre-synthesized Fe3O4 NPs were added under vigorous

stirring at 600 rpm for 1 h at 80 °C. To this, 100 mL of 0.1 M citric acid solution was added dropwise under continuous stirring at 300 rpm for 3 h to yield brown color precipitate (magnetic

bimetallic Fe3O4@TiO2 NPs). The obtained magnetic NPs were purified by centrifugation at 10,000 rpm for 20 min, washed with ethanol and kept at 100 °C in a hot air oven for 8 h and

calcinated at 500 °C for 2 h under a nitrogen environment. FABRICATION OF HYBRID MAGNETIC KENAF FIBER CELLULOSE–COLLAGEN SPONGE EMBEDDED WITH BIMETALLIC FE3O4@TIO2 NPS (KFCC-BFT) The weighed

amount of organic fibers (collagen and kenaf fiber cellulose) in 1:1 proportion was dissolved in 90 mL of 0.5 M glacial acetic acid using a homogenizer (Ika, T25) at 4 °C for 10 min. The

wt.% of magnetic BFT NPs was calculated based on the weight of the organic fibers and three bio-sponges were fabricated namely KFCC, KFCC-BFT5, and KFCC-BFT10 corresponding to 0, 5 and 10%

(wt./wt.) of BFT in the mixture. The BFT was sonicated using Lark Probe Sonicator for 2 min and added to the organic collagen–cellulose mixture. The mixture was homogenized at 4 °C for 1 h

and transferred into 12 well plates and kept in a freezer (− 40 °C) for 2 h. Then, frozen products were kept in a lyophilizer (Delvac freeze drier) for 24 h to obtain hybrid magnetic

KFCC-BFT bio-sponges. CRYSTAL VIOLET DEGRADATION The photocatalytic activity of the hybrid bio-sponges was investigated by analyzing the degradation of water-soluble crystal violet (CV) dye

under visible light and sunlight irradiation under ambient environmental conditions. The initial concentration of CV is 2.5 × 10−5 mol/L. The photodegradation reaction was carried out in a

100 mL glass beaker containing 30 mL of CV dye. Before the photodegradation reaction, the glass beaker containing 30 mL of CV dye and bio-sponge was stirred for 30 min in the dark to

establish adsorption–desorption equilibrium. Then, the solution was irradiated using 200 W Hg (Xe) with a medium pressure lamp (66,454 Newport Oriel Instrument) at room temperature or

exposed directly to sunlight at ambient temperature for 180 min at neutral pH. The glass beaker holding the sample was held 20 cm from the light source during the irradiation procedures. At

regular intervals of 10 min, samples of up to 1 mL were taken out for UV–visible examination. MOTOR OIL REMOVAL The oil adsorbency of the nanocomposite was determined according to ASTM:

F726-12 method39. A weighed dry bio-sponge (m0) was placed in a beaker containing excess used motor oil and allowed to immerse for 15 min. Then, the sponge was removed and drained for 2 min

and the wet weight was taken (m1). The oil adsorbency as the ratio of oil adsorbed to the dry sponge weight was calculated as below. $$Oil\,adsorbency=\frac{m}{{m}_{0}}$$ (1) With m0 the

initial dry sponge weight, m1 weight of the sponge at end of the oil test and m = (m1 − m0) net oil adsorbed. The recyclability and reusability performance of the hybrid bio-sponge was also

investigated according to ASTM:F726-12 using the centrifugation method. The centrifugation was carried out at 5000 rpm for 5 min at 25 °C. Additionally, the bio-sponge was added to a petri

dish containing excess distilled water and 0.5 g of used motor oil in order to test the sponge's ability to absorb oil from an oil–water mixture and track the sponge in a magnetic

field. With the help of a strong magnet, the sponge was moved through the petri-dish for 15 min to adsorb the oil. Then, the sponge was removed and drained for 2 min and the adsorbed oil was

squeezed out. Digital photographs were taken during each stage of the process. CHARACTERIZATION The crystalline structure of TiO2, Fe3O4 and BFT NPs were examined by using a Rigaku Miniflex

(II) desktop diffractometer with Ni filtered Cu Kα radiation source (λ = 1.5418 nm) in the angular range of 20° to 80° at goniometer speed of 5 °C /min at room temperature. To identify the

phase of the samples, XRD results were uploaded to the Joint Committee on Powder Diffraction Standards (JCPDS) software and the report was generated. The average crystallite d-size of NPs

was determined using Debye–Scherrer Equation. $$D=\frac{k\lambda }{\beta cos\theta }$$ (2) where, k represents the constant (0.89), λ stands for the wavelength of X-ray (1.5418 nm), β

denotes full width at half the maximum of the diffraction peak and _θ_ is the Bragg angle. Dynamic light scattering measurements (DLS) of the prepared NPs were analyzed using Zetasizer Nano

ZS, series ZEN 3600, Malvern Instruments to obtain the particle size. UV–vis spectra of the NPs were obtained using a UV–visible spectrophotometer (Shimadzu UV-1800). The spectrum was taken

from 200 to 800 nm with a 0.5 nm scanning interval. UV–vis diffusion reflectance spectra (UV–vis DRS) of bimetallic NPs and bio-sponges were obtained in a UV–Vis–NIR spectrophotometer

(Agilent technologies) to determine the band gap energy. The morphologies of the samples were examined with a field emission scanning electron microscope (FESEM, TESCAN, model-CLARA, Czech

Republic) equipped with an energy-dispersive X-ray (EDX) spectroscopy. For high-resolution transmission electron microscopy (HRTEM, JEOL JEM 3010) analysis of BFT NPs, 5 µL of the sample was

dispersed in 1 mL HPLC grade ethanol using water bath sonication for 30 min and 20 µL of the dispersed NPs was coated over the copper grid and dried at room temperature. The sample was

observed at 200 kV voltage using LaB6 filament. To analyze the surface compositions of the nanocomposites, X-ray photoelectron spectroscopy (XPS) was performed using the ESCALAB 250 xi,

Thermo Scientific. While pore size and pore diameter were determined using the Barrett–Joyner–Halenda (BJH) approach, the surface area was estimated using the Brunauer–Emmett–Teller (BET)

theory. Fourier-transformed infrared (FT-IR) spectroscopic analysis was carried out using a Jasco spectrometer (Model No-4700) for the extracted cellulose, collagen, and synthesized

bio-sponge samples. The surface wettability of sponges was characterized by water contact angle and oil (hexadecane) contact angle with a 5µL droplet. The measurements were obtained with a

contact angle meter (Holmar, series HO-IAD-CAM-01) at room temperature. The magnetic properties of BFT, KFCC-BFT5 and KFCC-BFT10 were measured at room temperature using a vibrating sample

magnetometer (VSM, Lakshore VSM 7410S). RESULTS AND DISCUSSION CHARACTERIZATION OF TIO2, FE3O4 AND MAGNETIC BFT NPS Figure 1 shows the XRD patterns of the synthesized NPs. The diffraction

peaks at 2θ angles of 25.4°, 37.8°, 48.1°, 54.1°, 55.3°, 62.9°, 68,7°, 70.5° and 75.3° can be assigned to the (101), (004), (200), (105), (211), (204), (116), (220) and (215) crystal planes

of the anatase TiO2 phase (JCPDS No.021-1272)40. The magnetite NPs exhibit diffraction peaks at 2θ angles of 30.2°, 35.6°, 43.3°, 53.7°, 57.5°, 62.9° and 74.5° corresponding to the (220),

(311), (400), (422), (511), (440) and (533) crystal planes of cubic Fe3O4 phase (JCPDS No. 65-3107)41. The sharp and intense crystallinity peaks at 2θ angles of 25.4° and 35.6° corresponding

to the (101) and (311) planes of TiO2 and Fe3O4, respectively are present in the diffraction pattern of magnetic BFT NPs along with all the other peaks of both the nanoparticles.

Crystallite size of the Fe3O4 and TiO2 was calculated as 24 and 15 nm, respectively using Scherrer’s formula as given in Eq. 2. Furthermore, the interplaner spacing value was calculated as

0.25 and 0.34 nm, which was resulting from the intense peak of the Fe3O4 (311) plane and TiO2 (101) plane, respectively. However, it is interesting to note the intensity of the peaks

corresponding to the Fe3O4 is lower than those of TiO2. This could be due to the higher amount of TiO2 present in the bimetallic NPs compared to the Fe3O4. The morphology of the magnetic BFT

NPs was investigated by HRTEM. Figure 2a shows randomly dispersed Fe3O4 NPs coated with the TiO2 NPs. The result suggests that the magnetic BFT NPs are in aggregated form in contact with

one another rather than the typical core–shell configurations. The Fe3O4 and TiO2 particles present in the bimetallic NPs seem to in the order of 20–25 nm although they are in contact

aggregates. The particle size range observed here is comparable to the pristine Fe3O4 and TiO2 NP crystallite size obtained from XRD data. The HRTEM image (Fig. 2b) indicates that the

lattice interlayer spacing of Fe3O4 and TiO2 is 0.24 and 0.33 nm, respectively coinciding with the (311) and (101) planes of the respective oxides, as revealed by XRD patterns42. The average

particle size of TiO2 NPs, Fe3O4 NPs and uncalcined BFT NPs measured through DLS is 41, 250 and 391 nm, respectively as shown in Figure S1. After calcination at 500 °C for 2 h, it seems

that BFT NPs got agglomerated with the increase in particle size to 703 nm. Overall, the particle size observed by DLS is much larger than the values obtained by XRD and HRTEM owing to the

interaction of water molecules on the NP surface during DLS measurement. The UV–Vis absorption spectra of pristine TiO2, Fe3O4 and BFT NPs are shown in Fig. 2c. The absorption band of pure

TiO2 NPs is in the range of 300–350 nm, which is in the UV region, while the magnetite Fe3O4 NPs exhibit the absorption band at 350–450 nm between UV and visible regions. In contrast, it

should be noted that the BFT NPs are characterized by a wide band between 350 and 530 nm, which appears relatively high absorption in the visible region (400–800 nm). The addition of

magnetite moiety induces a red shift in the absorption edges to a longer wavelength compared to pristine TiO2. Fe3O4 promotes the movement of electrons from the valence band to the

conduction band, thus leading to a shift in TiO2 absorption in the range of its photocatalytic response5,17. Bimetallic NPs and magnetic hybrid organic–inorganic bio-sponges were

characterized for their magnetic behavior using room temperature magnetization by VSM. Figure 2d shows typical S-like curves with perfect saturation magnetization indicating the

ferromagnetic behavior of the bimetallic NPs and the bio-sponges. Compared to pure BFT NPs (with a saturation magnetization of 8.60 emu/g), the saturation magnetization values of bio-sponges

were reduced to 1.44 and 0.86 emu/g, respectively for KFCC-BFT10 and KFCC-BFT5 nanocomposites as a function of dosage of BFT. The hysteresis loops are shown in Figures S2a and b. It is seen

that both the pure BFT NPs and bio-sponges exhibit coercivity of about 118 Oe. Whereas the remanent magnetization for the BFT NPs is about 1.4 emu/g and 0.16 and 0.24 emu/g for the

KFCC-BFT5 and KFCC-BFT10 nanocomposites, respectively, which behaves similar to the saturation magnetization trend. CHARACTERIZATION OF KFCC, KFCC-BFT5, AND KFCC-BFT10 FTIR spectrum of the

extracted cellulose from kenaf fiber is shown in Fig. 3a. The band at 3336 cm−1 is attributed to the O–H stretching vibration and hydrogen bond of the hydroxyl groups. The band at 2889 cm−1

is the characteristic peak for alkanes exhibiting C–H stretching vibration of CH and CH2 asymmetric stretching in the cellulose backbone. The adsorbed water binding H–O–H band is observed at

1636 cm−1. The absorption peak at 1341 cm−1 corresponds to CH3 deformation. The intense band, centered at 1031 cm−1 is associated with the C–O stretching modes of the hydroxyl and ether

groups in the cellulose. The band at 900 cm−1 can be attributed to the presence of β-glycosidic linkages and the small peak at 666 cm−1 is associated with the C–OH out-plane bending. It is

interesting to note the disappearance of characteristics peaks at 1725 cm−1 and 1505 cm−1 corresponding to C=O stretching vibration of the acetyl groups in the hemicelluloses and the C=C

stretching of the benzene ring of the lignin, respectively, indicating successful removal of these components during the cellulose extraction process. The FT-IR spectrum of pristine collagen

in Fig. 3b depicts the characteristics peaks including the amide I (C=O stretching) at 1664 cm−1, the amide II (N–H bending couple to C–N vibration) at 1546 cm−1, the amide III (C–N

stretching and N–H bending) at 1244 cm−1, the amide A (C–N stretching and N–H bending vibration) at 3343 cm−1 and the amide B (C–H stretching) at 3081 cm−16. The KFCC bio-sponge spectrum

shows (Fig. 3c) characteristic peaks for both pristine collagen and cellulose with few changes in some peaks. The broad band at 3343 cm−1 corresponds to the N–H stretching vibration of amide

A of collagen changed as a sharp band and present at the lower wavelength of 3322 cm−1. This result suggests that the N–H group of collagen may be involved in hydrogen bonds43.

Interestingly, the characteristics peaks of pristine collagen corresponding to the amide I group shifted from 1664 to 1644 cm−1, from 1546 to 1536 cm−1 for the amide II group, and the amide

III group from 1244 to 1237 cm−1, thus, indicating a blue shift of 20 cm−1, 10 cm−1 and 7 cm−1, respectively. These downshifts indicate a possible hydrogen bond interconnection between N–H

groups of collagen and the hydroxyl OH group of cellulose43. In the FTIR spectrum (Fig. 3d) of the magnetic hybrid bio-sponge KFCC-BFT10, we can observe key characteristic peaks of pure

collagen and cellulose. Meanwhile, new peaks are observed at 549, 583 and 660 cm−1 corresponding to Fe–O stretching vibration of magnetite Fe3O4, Ti–O, and O–Ti–O bonds, respectively5,12.

The presence of oxide bond peaks in the bio-sponge indicates the successful incorporation of the metal nanoparticles in the organic sponge. The surface morphology of the bio-sponges (Fig. 

4a–c) shows a multi-layered sheath-like spongious architecture and a highly linked porous network structure when probed through FESEM (Fig. 4a–c). It is clearly shown from the insert images

(5 μm) that the hybrid bio-sponges (Fig. 4b and c) depict relatively dense and compact structures compared to the pristine KFCC bio-sponge (Fig. 4a). Further, it can be seen from Fig. 4c

that the bimetallic Fe3O4@TiO2 NPs are tightly anchored to the surface and interior of the bio-sponge fibers possibly through hydrogen bond interaction with Fe–OH or Ti–OH25. In comparison

to the KFCC bio-sponge (Fig. 4d), the EDX mapping images show that both organic (C, N, O) and inorganic (Ti, Fe) elements are present in the hybrid bio-sponges (Fig. 4e,f). To investigate

the elemental composition, a selected region of the SEM image was taken and the EDX spectral analysis was carried out. EDX spectra results displayed in Figure S3a–c confirm the presence of

Fe and Ti in the KFCC–BFT nanocomposites. The presence of C, N and O peaks indicates the main elements in the KFCC (Kenaf fiber and collagen) as shown in Figure S3a. As can be seen, the

intensity of the Fe and Ti peaks is higher in the KFCC-BFT10 nanocomposite (Figure S3c) when compared to KFCC-BFT5 (Figure S3b) corresponding to the dosage of the BFT. There were no other

peaks in the spectra that may be attributed to contaminants. These findings prove the high adhesion of Fe and Ti-based bimetallic nanoparticles to the KFCC surface. The N2

adsorption–desorption technique was employed to investigate the pore size, pore diameter and pore volume of the KFCC-BFT10 bio-sponge. As shown in Fig. 5a, KFCC-BFT10 bio-sponge exhibited

characteristic hysteresis loop in the adsorption–desorption isotherm. According to IUPAC classification, the N2 adsorption–desorption isotherm of the KFCC-BFT10 bio-sponge show type IV

isotherm pattern with H3 hysteresis loop, which means that the KFCC-BFT10 bio-sponge belongs to typical mesoporous material. The KFCC-BFT10 bio-sponge possesses a specific surface area of

40.9 m2/g according to Brunauer–Emmett–Teller (BET). Pore size distribution of the KFCC-BFT10 bio-sponge (Fig. 5b) shows two maxima. A very narrow peak at 2.2 nm and a broad pore size

distribution from 3 to 6 nm indicate fairly wide distribution of pores. The prepared KFCC-BFT10 bio-sponge shows pore volume of 0.042 cm3/g (Fig. 5c). The high surface area and pore volume

obtained may provide adequate surface sites for increased photocatalytic activity and oil sorption. The chemical composition and electronic structure of the developed photocatalyst were

determined by the XPS spectra. The XPS survey spectra of KFCC, BFT and KFCC-BFT10 bio-sponge are illustrated in Fig. 6a and the core level spectra of Fe 2p and Ti 2p are shown in Fig. 6b–e.

As can be seen in Fig. 6a, Fe 2p, Ti 2p, C 1s, N 1s, O 1s, and O 2s peaks are visible in the spectra of pristine BFT, KFCC and KFCC-BFT10 bio-sponge. These elemental compositions obtained

for the nanoparticles, hybrid biopolymer matrix and nanocomposites through XPS analysis are concurrent with the FESEM − EDX data and further confirm that the samples are devoid of any

impurities. The pristine BFT and KFCC-BFT10 bio-sponge showed two distinctive peaks of Fe3+ 2p3/2 and Fe3+ 2p1/2 in the Fe 2p spectra at 710.6 and 724.1 eV, respectively (Fig. 6b and c). It

shows that the predominant form of Fe species in the nanocomposites is Fe3+ state. Additionally, the binding energies at 713.7 and 718.4 eV in the Fe 2p spectra of pure BFT could be

attributed to Fe3+ in the spinel structure and the binding energy at 727.4 eV could be attributed to Fe3+ bound with a hydroxyl group. However, the binding energy in the Fe 2p spectra of the

KFCC-BFT10 bio-sponge is slightly changed to 713.4, 719.0, and 727.5 eV, respectively. This meant that in the KFCC-BFT10 bio-sponge, the electrons could have more influence towards Fe3+. In

the Ti 2p core level spectra of the pristine BFT10 and KFCC-BFT10 bio-sponge (Fig. 6d and e), two unique peaks at 458.4 and 464.3 eV are seen, which are attributed to Ti 2p3/2 and Ti 2p1/2,

respectively, indicating that the titanium is mainly presented as Ti4+ in the anatase TiO2 form. This is in concurrence with our XRD data and also various literature values44,45. Thus, it

is determined that Fe in Fe3O4@TiO2 has an oxidation state of + 3, whereas Ti is present as tetravalent and therefore both the Fe3+ and Ti4+ are in oxide form rather than in pure metallic

form. The O 1s core level XPS spectra of pristine BFT, KFCC and KFCC-BFT10 bio-sponges are shown in Fig. 7. The binding energy range for the O 1s peak is 528–534 eV. Oxygen can exist in two

different molecular states namely O2− and O2− with binding energy values of about 530 and 531.5 eV, respectively. For KFCC and KFCC-BFT10 bio-sponge, the O 1s peak appears at 530.7 and 531.5

 eV, respectively. This component typically results from surface oxygen that is non-stoichiometric or OH from air. The surface O2 present in the oxides is responsible for the existence of a

peak at 532.2 eV. In the case of BFT, two peaks are observed in the core-level spectra of O 1s. The low binding energy component observed at 529.7 eV is attributed to the O2− forming oxide

whereas the peak at 530.8 eV is assigned to OH−. As can be seen, XPS data show that iron is present in the chemical state of Fe3+ and oxygen is predominantly in the state of O2−, thereby

verifying the formation of Fe2O3. In brief, the Fe element in the KFCC-BFT10 bio-sponge is more positively charged, which would help in the regeneration of Fe3+ and thus may stimulate the

photocatalytic degradation reaction. The band gap energy of as-prepared bio-sponges was also investigated. From Fig. 8a, it is seen that the band gap energy of collagen and KFCC sponges are

similar around ~ 5.1 eV and much higher than that of the hybrid KFCC-BFT10 bio-sponge, which is ~ 2.5 eV. It is seen that the band gap energy of bio-sponge without bimetallic nanoparticles

is double the band gap energy of KFCC-BFT10. The possible reason for the decrease in band gap energy could be the effective interactions of Ti–O–Fe bonds in the KFCC matrix5,17. This reduced

bandgap energy along with the red-shifted absorption in the visible region indicates that the hybrid KFCC-BFT10 bio-sponge can be excited under visible light or direct sunlight illumination

to produce more electron–hole pairs for enhanced photocatalytic degradation activity of organic pollutants. The water contact angles of the hybrid bio-sponges are shown in Fig. 8b and c and

relatively high water contact angle values were achieved after the interaction with the bimetallic nanoparticles. As the percentage of bimetallic NP in the sponge increases, the water

contact angle also increases. This finding suggests that the as-prepared bio-sponges are reasonably hydrophobic. On the other hand, during the oil contact angle measurement, the oil droplet

penetrated quickly into the hybrid bio-sponges and the contact angle could not be recorded. The wettability tests prove that the hybrid bio-sponges exhibit selective wettability towards

water and oil. These hybrid bio-sponges can easily adsorb oil and repel water. The water contact angle for the pristine collagen–cellulose (KFCC) sponge could not be recorded because the

water droplet was immediately absorbed by the sponge due to the hydrophilic property of cellulose and collagen. PHOTOCATALYTIC ACTIVITY As-prepared bio-sponges were used to study the

degradation of aqueous crystal violet (CV) dye under visible light and sunlight in the presence of H2O2. Hydrogen peroxide plays a vital role in the degradation of CV by the generation of

two strong hydroxyl radicals (HO·)46,47,48. The mechanism for the degradation of CV in presence of magnetic bimetallic Fe3O4@TiO2 NPs has been described by Vinosel et al.5 As seen in Fig. 

9a, the adsorption capacity of the bio-sponge is primarily responsible for the removal of roughly 12.4% of the CV in 30 min under dark conditions, which was realised until adsorption

equilibrium is established. It is observed that the sharpness and the intensity of the maximum absorption peak of CV at 590 nm decreased with extended visible illumination time followed by

slight blue-shifting for the samples treated with KFCC-BFT5 and KFCC-BFT10 bio-sponges (Fig. 9b and c). The photocatalytic degradation efficiency of CV dye under visible light irradiation is

85.4 and 91.2% for KFCC-BFT5 and KFCC-BFT10 bio-sponges, respectively. After 1 h of irradiation (Fig. 10a), about 50% of CV dye has been degraded and more than 60% dye in the case of

KFCC-BFT10 bio-sponge. The hybrid KFCC-BFT10 bio-sponge photocatalyst shows greater degradation efficiency of 91.2% compared to 86% using 500 mg of pure Fe3O4@TiO2 powder photocatalyst in

500 mL water as reported by Vinosel et al.5 As can be seen, KFCC-BFT10 bio-sponge exhibited higher degradation capability owing to the higher BFT content and hence further subjected to

photocatalytic degradation under sunlight exposure. The results demonstrate 86.6% degradation of CV dye for KFCC-BFT10 bio-sponge under sunlight (Fig. 9d). As shown in Table 1, the

photocatalytic degradation of the KFCC-BFT10 bio-sponge photocatalyst synthesised in this study is comparable to other similarly reported photocatalysts with the added advantage of easy

biodegradability of the photocatalyst support. The better photocatalytic degradation obtained with KFCC-BFT10 bio-sponge can be explained by the 3D macroporous structure and the floatability

behavior (low density ~ 9 mg.cm−3), which provide the photocatalyst the ability to ease photocatalytic oxygenation activity in the air–water interface with high induced photon and increased

interaction between the hybrid magnetic NPs catalyst and CV dye due to the presence of BFT on the surface as well as the inner layers of the bio-sponge support. OIL REMOVAL EFFICACY To

evaluate the sorbent performance characteristic of bio-sponge as a bio-based, easily biodegradable and eco-friendly material for oil spill removal (Fig. 10b–d), the oil adsorption capacity

was investigated. From Fig. 10b, it is clearly seen that both hybrid bio-sponges exhibit a higher adsorption capacity of 41.4 and 46.1 g/g for KFCC-BFT5 and KFCC-BFT10 bio-sponges,

respectively, compared to KFCC bio-sponge (37.2 g/g). This high adsorption capacity of the hybrid sponge can be corroborated by its 3D macroporous network structure and hydrophobicity. An

added advantage of the developed magnetic hybrid bio-sponge is the ability to track the motion of the sponge on the surface of oil–water emulsion under a magnetic field (Fig. 10c). It is

well established that the oil sorption capacity of a sorbent is mainly governed by some physical sorption properties such as the capillary effect due to the porous structure, van der Waals

forces and the hydrophobic interactions between the sorbent and oils54, and in the present case the tracking under magnetic field is considered as an additional factor that controls the

adsorption capacity of sorbent. The recyclability and reusability of sorbent after oil removal is an important aspect to be considered during the evaluation of performance characteristics of

an adsorbent such as adsorption capacity after repeating cycles of adsorbing-removing and waste management of the sorbent after being used in the environment. The as-prepared sponges are

green and easily biodegradable and thus waste management after use can be done naturally without causing any harm to human beings and the environment. The recyclability and reusability data

reveal that the hybrid bio-sponge exhibits high sorption capacity even after 5 cycles, showing only a small decrease from 46.1 g/g to around 40 g/g, after which the oil sorption efficiency

decreases up to around 30 g/g and remains relatively constant up to 9 cycles (Fig. 10d). During recycling, it has been noticed that the hybrid bio-sponge still contains trapped oil rendering

it sticky, highly packed, and dense material after centrifugation. After each cycle, the sponge was immersed in ethanol solution 2 times for 1 h, freeze-dried and lyophilized for 24 h.

Figure 10c shows that the adsorbed oil may be easily removed by squeezing out and only a small amount of oil is left in the KFCC-BFT10 nanocomposite. The KFCC-BFT10 nanocomposite could be

easily separated from the oil/water mixture by forceps and used for the next run thereby demonstrating its potential for oil removal applications with recyclability. CONCLUSION In summary,

an easily biodegradable collagen–cellulose-based magnetic bio-sponge loaded with bimetallic Fe3O4@TiO2 NPs was fabricated with high potency for dye and oil removal. The structural morphology

analysis by HRTEM revealed no core–shell structure but the deposition of TiO2 nanoparticles onto the surface of magnetite Fe3O4 nanoparticles. From room temperature magnetization

measurement, it is found that the saturation magnetization value of bio-sponge was decreased compared to the value of pure BFT NPs and hysteresis loops with an S-like curve indicating

ferromagnetic behavior of the bimetallic nanoparticles and bio-sponge. The morphology of the magnetic hybrid bio-sponge showed a 3D macroporous interconnection network with the BFT NPs bound

on the surface and interior of the collagen–cellulose fibrous network as visualized through HRSEM. The wettability tests proved that the incorporation of the bimetallic NPs enhanced the

hydrophobicity and roughness of the hybrid bio-sponges. The as-prepared bio-sponge exhibited high photodegradation activity by the removal of crystal violet dye up to 91.2 and 86.6% under

visible light and direct sunlight irradiation, respectively. It is also demonstrated that a high oil sorption capacity of 46.1 g/g was achieved and the bio-sorbent can be recycled and reused

up to 9 cycles. Based on the results, the as-prepared magnetic hybrid bio-sponge has a dual potential ability in wastewater remediation for dye removal and oil spill management thereby

suggesting effective visible-light-driven photocatalytic application at an industrial scale. DATA AVAILABILITY The datasets generated during and/or analysed during the current study are

available from the corresponding author on reasonable request. REFERENCES * Zhang, M. _et al._ Efficient removal of organic pollutants by metal–organic framework derived Co/C yolk–shell

nanoreactors: Size-exclusion and confinement effect. _Environ. Sci. Technol._ 54, 10289–10300 (2020). Article  ADS  CAS  PubMed  Google Scholar  * Li, X., Jia, Y., Zhou, M., Su, X. &

Sun, J. High-efficiency degradation of organic pollutants with Fe, N co-doped biochar catalysts via persulfate activation. _J. Hazard. Mater._ 397, 122764 (2020). Article  CAS  PubMed 

Google Scholar  * Chen, D. _et al._ Photocatalytic degradation of organic pollutants using TiO2-based photocatalysts: A review. _J. Clean. Prod._ 268, 121725 (2020). Article  CAS  Google

Scholar  * Wang, Z., Wu, A., Colombi Ciacchi, L. & Wei, G. Recent advances in nanoporous membranes for water purification. _Nanomaterials_ 8, 65 (2018). Article  CAS  PubMed  PubMed

Central  Google Scholar  * Vinosel, V. M. _et al._ Preparation and performance of Fe3O4/TiO2 nanocomposite with enhanced photo-Fenton activity for photocatalysis by facile hydrothermal

method. _Appl. Phys. A_ 125, 1–13 (2019). Article  Google Scholar  * Nagaraj, S., Cheirmadurai, K. & Thanikaivelan, P. Visible-light active collagen-TiO2 nanobio-sponge for water

remediation: A sustainable approach. _Clean. Mater._ 1, 100011 (2021). Article  CAS  Google Scholar  * Hernandez-Maya, R., Solís-López, M. & Th-Th, C. Photocatalytic degradation of

orange G using TiO2/Fe3O4 nanocomposites. _J. Mater. Sci._ 29, 15436–15444 (2018). Google Scholar  * Pei, M. _et al._ State of the art of tertiary treatment technologies for controlling

antibiotic resistance in wastewater treatment plants. _Environ. Int._ 131, 105026 (2019). Article  CAS  PubMed  Google Scholar  * Ahmed, S. _et al._ Recent developments in physical,

biological, chemical, and hybrid treatment techniques for removing emerging contaminants from wastewater. _J. Hazard. Mater._ 416, 125912 (2021). Article  CAS  PubMed  Google Scholar  *

Crini, G. & Lichtfouse, E. Advantages and disadvantages of techniques used for wastewater treatment. _Environ. Chem. Lett._ 17, 145–155 (2019). Article  CAS  Google Scholar  * Huang,

X.-H. _et al._ Transparent floatable magnetic alginate sphere used as photocatalysts carrier for improving photocatalytic efficiency and recycling convenience. _Carbohydr. Polym._ 254,

117281 (2021). Article  CAS  PubMed  Google Scholar  * Fan, H. _et al._ Facile synthesis of uniformly loaded Fe3O4–TiO2/RGO ternary hybrids for enhanced photocatalytic activities. _Opt.

Mater._ 111, 110582 (2021). Article  CAS  Google Scholar  * Ahmed, A. _et al._ Efficient photocatalytic degradation of toxic Alizarin yellow R dye from industrial wastewater using

biosynthesized Fe nanoparticle and study of factors affecting the degradation rate. _Photochem. Photobiol. B Biol._ 202, 111682 (2020). Article  CAS  Google Scholar  * Hajipour, P. _et al._

Surface modification of TiO2 nanoparticles with CuO for visible-light antibacterial applications and photocatalytic degradation of antibiotics. _Ceram. Int._ 47, 33875–33885 (2021). Article

  CAS  Google Scholar  * Tekin, D., Birhan, D. & Kiziltas, H. Thermal, photocatalytic, and antibacterial properties of calcinated nano-TiO2/polymer composites. _Mater. Chem. Phys._ 251,

123067 (2020). Article  CAS  Google Scholar  * Charitha, T. _et al._ Efficient photodegradation activity of α-Fe2O3/Fe2TiO5/TiO2 and Fe2TiO5/TiO2 nanocomposites synthesized from natural

ilmenite. _Results Mater_ 12, 100219 (2021). Article  CAS  Google Scholar  * Chang, J., Zhang, Q., Liu, Y., Shi, Y. & Qin, Z. Preparation of Fe3O4/TiO2 magnetic photocatalyst for

photocatalytic degradation of phenol. _J. Mater. Sci._ 29, 8258–8266 (2018). CAS  Google Scholar  * Krishnan, S. & Shriwastav, A. Application of TiO2 nanoparticles sensitized with

natural chlorophyll pigments as catalyst for visible light photocatalytic degradation of methylene blue. _J. Environ. Chem. Eng._ 9, 104699 (2021). Article  CAS  Google Scholar  * Parvate,

S. _et al._ Titanium dioxide nanoparticle-decorated polymer microcapsules enclosing phase change material for thermal energy storage and photocatalysis. _ACS Appl. Polym. Mater._ 3,

1866–1879 (2021). Article  CAS  Google Scholar  * Liu, X. _et al._ The intrinsic effects of oxygen vacancy and doped non-noble metal in TiO2 (B) on photocatalytic oxidation VOCs by visible

light driving. _J. Environ. Chem. Eng._ 10, 107390 (2022). Article  CAS  Google Scholar  * Chu, A.-C., Sahu, R. S., Chou, T.-H. & Shih, Y.-H. Magnetic Fe3O4@TiO2 nanocomposites to

degrade bisphenol A, one emerging contaminant, under visible and long wavelength UV light irradiation. _J. Environ. Chem. Eng._ 9, 105539 (2021). Article  CAS  Google Scholar  * Yu, L. _et

al._ In situ controllable fabrication of two-dimensional magnetic Fe3O4/TiO2@ Ti3C2T x composites for highly efficient phosphopeptides enrichment. _ACS Appl. Mater. Interfaces_ 13,

54665–54676 (2021). Article  CAS  PubMed  Google Scholar  * Chishti, A. N. _et al._ Synthesis of highly efficient and magnetically separable Fe3O4@ C-TiO2-Ag catalyst for the reduction of

organic dyes and 4-nitrophenol. _Colloids Surf. A_ 631, 127694 (2021). Article  CAS  Google Scholar  * Thanikaivelan, P., Narayanan, N. T., Pradhan, B. K. & Ajayan, P. M. Collagen based

magnetic nanocomposites for oil removal applications. _Sci. Rep._ 2, 1–7 (2012). Article  Google Scholar  * Peng, H. _et al._ Preparation of superhydrophobic magnetic cellulose sponge for

removing oil from water. _Ind. Eng. Chem. Res._ 55, 832–838 (2016). Article  CAS  Google Scholar  * Peng, B. _et al._ Cellulose-based materials in wastewater treatment of petroleum industry.

_Green Energy Environ._ 5, 37–49 (2020). Article  Google Scholar  * Zhao, X.-Q., Wahid, F., Cui, J.-X., Wang, Y.-Y. & Zhong, C. Cellulose-based special wetting materials for oil/water

separation: A review. _Int. J. Biol. Macromol._ 185, 890–906 (2021). Article  CAS  PubMed  Google Scholar  * Yang, S. _et al._ Facile and sustainable fabrication of high-performance

cellulose sponge from cotton for oil-in-water emulsion separation. _J. Hazard. Mater._ 408, 124408 (2021). Article  CAS  PubMed  Google Scholar  * Meng, X., Dong, Y., Zhao, Y. & Liang,

L. Preparation and modification of cellulose sponge and application of oil/water separation. _RSC Adv._ 10, 41713–41719 (2020). Article  ADS  CAS  PubMed  PubMed Central  Google Scholar  *

Ahankari, S., Paliwal, P., Subhedar, A. & Kargarzadeh, H. Recent developments in nanocellulose-based aerogels in thermal applications: a review. _ACS Nano_ 15, 3849–3874 (2021). Article

  CAS  PubMed  Google Scholar  * Ahuja, D. _et al._ Superhydrophobic modification of cellulose sponge fabricated from discarded jute bags for oil water separation. _J. Environ. Chem. Eng._

9, 105063 (2021). Article  CAS  Google Scholar  * Pezzoli, D. _et al._ Fibronectin promotes elastin deposition, elasticity and mechanical strength in cellularised collagen-based scaffolds.

_Biomaterials_ 180, 130–142 (2018). Article  CAS  PubMed  Google Scholar  * Curtin, C. _et al._ A physiologically relevant 3D collagen-based scaffold–neuroblastoma cell system exhibits

chemosensitivity similar to orthotopic xenograft models. _Acta Biomater._ 70, 84–97 (2018). Article  CAS  PubMed  Google Scholar  * Ramanathan, G. _et al._ Fabrication of biohybrid cellulose

acetate-collagen bilayer matrices as nanofibrous spongy dressing material for wound-healing application. _Biomacromol_ 21, 2512–2524 (2020). Article  CAS  Google Scholar  * Kalirajan, C.

& Palanisamy, T. Bioengineered hybrid collagen scaffold tethered with silver-catechin nanocomposite modulates angiogenesis and TGF-β toward scarless healing in chronic deep second degree

infected burns. _Adv. Healthc. Mater._ 9, 2000247 (2020). Article  CAS  Google Scholar  * Zhang, S. _et al._ Construction and nanostructure of chitosan/nanocellulose hybrid aerogels.

_Biomacromol_ 22, 3216–3222 (2021). Article  CAS  Google Scholar  * Nagaraj, S., Easwaramoorthi, S., Rao, J. R. & Thanikaivelan, P. Probing visible light induced photochemical

stabilization of collagen in green solvent medium. _Int. J. Biol. Macromol._ 131, 779–786 (2019). Article  Google Scholar  * Mandal, A. & Chakrabarty, D. Isolation of nanocellulose from

waste sugarcane bagasse (SCB) and its characterization. _Carbohydr. Polym._ 86, 1291–1299 (2011). Article  CAS  Google Scholar  * Astm, F. Standard test method for sorbent performance of

adsorbents. _Annual Book of ASTM Standards. ASTM Committee on Standards West Conshohocken_ (1998). * Chalasani, R. & Vasudevan, S. Cyclodextrin-functionalized Fe3O4@TiO2: Reusable,

magnetic nanoparticles for photocatalytic degradation of endocrine-disrupting chemicals in water supplies. _ACS Nano_ 7, 4093–4104 (2013). Article  CAS  PubMed  Google Scholar  * Lu, Z. _et

al._ Enhanced recyclability, stability, and selectivity of CdS/C@ Fe3O4 nanoreactors for orientation photodegradation of ciprofloxacin. _Chem. Eur. J._ 21, 18528–18533 (2015). Article  ADS 

PubMed  Google Scholar  * He, J., Zeng, X., Lan, S. & Lo, I. M. Reusable magnetic Ag/Fe, N-TiO2/Fe3O4@SiO2 composite for simultaneous photocatalytic disinfection of _E. coli_ and

degradation of bisphenol A in sewage under visible light. _Chemosphere_ 217, 869–878 (2019). Article  ADS  CAS  PubMed  Google Scholar  * Lohrasbi, S., Mirzaei, E., Karimizade, A., Takallu,

S. & Rezaei, A. Collagen/cellulose nanofiber hydrogel scaffold: Physical, mechanical and cell biocompatibility properties. _Cellulose_ 27, 927–940 (2020). Article  CAS  Google Scholar  *

Ainali, N. M., Kalaronis, D., Evgenidou, E., Bikiaris, D. N. & Lambropoulou, D. A. Insights into biodegradable polymer-supported titanium dioxide photocatalysts for environmental

remediation. _Macromol_ 1, 201–233 (2021). Article  CAS  Google Scholar  * Liu, J. _et al._ Facet–activity relationship of TiO2 in Fe2O3/TiO2 nanocatalysts for selective catalytic reduction

of NO with NH3: In situ DRIFTs and DFT studies. _J. Phys. Chem. C_ 121, 4970–4979 (2017). Article  ADS  CAS  Google Scholar  * Elmolla, E. S. & Chaudhuri, M. Photocatalytic degradation

of amoxicillin, ampicillin and cloxacillin antibiotics in aqueous solution using UV/TiO2 and UV/H2O2/TiO2 photocatalysis. _Desalination_ 252, 46–52 (2010). Article  CAS  Google Scholar  *

Liu, J. _et al._ Photo-Fenton reaction and H2O2 enhanced photocatalytic activity of α-Fe2O3 nanoparticles obtained by a simple decomposition route. _J. Alloys Compd._ 771, 398–405 (2019).

Article  CAS  Google Scholar  * Truong, H. B. _et al._ H2O2-assisted photocatalysis for removal of natural organic matter using nanosheet C3N4-WO3 composite under visible light and the

hybrid system with ultrafiltration. _J. Chem. Eng._ 399, 125733 (2020). Article  CAS  Google Scholar  * de Oliveira Pereira, L. _et al._ Preparation of magnetic photocatalysts from TiO2,

activated carbon and iron nitrate for environmental remediation. _J. Photochem. Photobiol., A_ 382, 111907 (2019). Article  Google Scholar  * Ravikumar, M. P. _et al._ Insights into the

photocatalytic memory effect of magneto-plasmonic Ag–Fe3O4@TiO2 ternary nanocomposites for dye degradation and H2 production under light and dark conditions. _Energy Fuels_ 36, 11503–11514

(2022). Article  CAS  Google Scholar  * Bibi, S. _et al._ Photocatalytic degradation of malachite green and methylene blue over reduced graphene oxide (rGO) based metal oxides

(rGO-Fe3O4/TiO2) nanocomposite under UV-visible light irradiation. _J. Environ. Chem. Eng._ 9, 105580 (2021). Article  CAS  Google Scholar  * Hatefi, R., Younesi, H., Mashinchian-Moradi, A.

& Nojavan, S. A facile decoration of anatase Fe3O4/TiO2 nanocomposite with graphene quantum dots: Synthesis, characterization, and photocatalytic activity. _Adv. Powder Technol._ 32,

2410–2422 (2021). Article  CAS  Google Scholar  * Shi, L., Wang, X., Hu, Y. & He, Y. Investigation of photocatalytic activity through photo-thermal heating enabled by Fe3O4/TiO2

composite under magnetic field. _Sol. Energy_ 196, 505–512 (2020). Article  ADS  CAS  Google Scholar  * Nguyen, S. T. _et al._ Cellulose aerogel from paper waste for crude oil spill

cleaning. _Ind. Eng. Chem. Res._ 52, 18386–18391 (2013). Article  CAS  Google Scholar  Download references ACKNOWLEDGEMENTS EFA acknowledges CSIR for awarding TWAS (CSIR-TWAS) postdoctoral

fellowship. SN acknowledges CSIR for granting Senior Research Fellowship. Authors thank CSIR-CLRI for financial support through the MLP02 project on “Collagen and other protein-based

innovative materials for heterogeneous applications”. The authors acknowledge the ICP, CSIR-CECRI for providing the XPS characterization facility. The authors thank CLRI-CATERS for the

analysis facilities. CSIR-CLRI Communication Number 1795. AUTHOR INFORMATION AUTHORS AND AFFILIATIONS * Advanced Materials Laboratory, CSIR-Central Leather Research Institute (CSIR-CLRI),

Sardar Patel Road, Adyar, Chennai, 600 020, India E. F. Assanvo, S. Nagaraj & P. Thanikaivelan * Laboratoire de Thermodynamique et de Physico-Chimie du Milieu, UFR SFA, Université Nangui

Abrogoua, 02 BP 801, Abidjan 02, Côte d’Ivoire E. F. Assanvo & D. Boa * University of Madras, Chepauk, Chennai, 600005, India S. Nagaraj & P. Thanikaivelan Authors * E. F. Assanvo

View author publications You can also search for this author inPubMed Google Scholar * S. Nagaraj View author publications You can also search for this author inPubMed Google Scholar * D.

Boa View author publications You can also search for this author inPubMed Google Scholar * P. Thanikaivelan View author publications You can also search for this author inPubMed Google

Scholar CONTRIBUTIONS E.F.A. executed the major experiments. E.F.A. and S.N. wrote the main manuscript text and prepared all the figures. P.T. designed the work and edited the manuscript.

All authors reviewed the manuscript. CORRESPONDING AUTHOR Correspondence to P. Thanikaivelan. ETHICS DECLARATIONS COMPETING INTERESTS The authors declare no competing interests. ADDITIONAL

INFORMATION PUBLISHER'S NOTE Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations. SUPPLEMENTARY INFORMATION

SUPPLEMENTARY INFORMATION. RIGHTS AND PERMISSIONS OPEN ACCESS This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation,

distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and

indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit

line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use,

you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. Reprints and permissions ABOUT THIS

ARTICLE CITE THIS ARTICLE Assanvo, E.F., Nagaraj, S., Boa, D. _et al._ Hybrid collagen–cellulose–Fe3O4@TiO2 magnetic bio-sponges derived from animal skin waste and Kenaf fibers for

wastewater remediation. _Sci Rep_ 13, 13365 (2023). https://doi.org/10.1038/s41598-023-40520-y Download citation * Received: 06 January 2023 * Accepted: 11 August 2023 * Published: 17 August

2023 * DOI: https://doi.org/10.1038/s41598-023-40520-y SHARE THIS ARTICLE Anyone you share the following link with will be able to read this content: Get shareable link Sorry, a shareable

link is not currently available for this article. Copy to clipboard Provided by the Springer Nature SharedIt content-sharing initiative